Nylon 66 / Polyester cord / PA56
DETAILED DESCRIPTION

PET Tire Cord

Twist No.

TPM

Breaking strength kg

Breaking elongation %

EASL %-at 4.5kg

EASL %-at 6.8kg

EASL %-at 9.0kg

EASL %-at 10.2kg

Hot air shrinkage %

Gauge mm

DPU %

Adhesive Kg/End

1000D/2

460±20

Target 15.4

≥14.0

14.5±2.5

4.5±0.5

/

/

/

≤2.0

0.55±0.05

2.5±1.0

≥14.0

1300D/2

380±20

Target 20.0

≥18.0

14.5±2.5

/

4.5±0.5

/

/

≤2.0

0.63±0.05

2.5±1.0

≥16.0

1500D/2

380±20

Target 23.0

≥21.5

14.5±2.5

/

/

/

/

≤2.0

0.63±0.05

2.5±1.0

≥18.0

2000D/2

280±20

Target 30.0

≥27.0

14.5±2.5

/

/

5.5±0.5

/

≤2.0

0.74±0.05

2.5±1.0

≥19.0

1000D/3

370±20

Target 23.0

≥21.5

14.5±2.5

/

4.5±0.5

/

/

≤2.0

0.65±0.05

2.5±1.0

≥18.0

1500D/3

300±20

Target 34.0

≥31

14.5±2.5

/

/

/

4.5±0.5

≤2.0

0.80±0.05

2.5±1.0

≥19.0


 Nylon 66 Tire Cord

Twist No.
     TPM

Breaking strength kg

Breaking elongation %

EASL %-at 4.5kg

EASL %-at 6.8kg

EASL %-at 9.0kg

EASL %-at 10.2kg

Hot air shrinkage %

Gauge mm

DPU %

Adhesive Kg/End

840D/2

460±20

≥14.0

23±4

9.0±2.0

/

/

/

≤4.5

0.55±0.03

5.5±1.0

≥13.0

1260D/2

370±20

≥21.0

23±4

/

9.0±2.0

/

/

≤4.5

0.66±0.03

5.0±1.0

≥18.0

1680D/2

320±20

≥27.5

23±4

/

/

9.0±2.0

/

≤4.5

0.76±0.03

5.0±1.0

≥18.0

1890D/2

300±20

≥31.0

23±4

/

/

/

9.0±2.0

≤4.5

0.82±0.03

4.5±1.0

≥18.0


PA56
     Tire Cord

Twist No.
     TPM

Treated Twist S
     (T/cm)

Treated Twist Z
     (T/cm)

Gauge 
     mm

Breaking strength
     (N)

Elongation at Break
     %

Elongation at 44.1N

Shrinkage 160 ℃.
     2min.0.05g/dtex
     %

Adhesion(H-Test)
     (151℃.25min.)N/10mm

Solid Content
     %

Warp/Weft  Density
     rope/10cm

Width

840D/2

460±20

45±2

45±2

0.50±0.1

≥141

23±4

9±0.5

4±1

152±10

5±0.1

94/12

145.0